ASTM A234 - Material inspection and review MTC

ASTM A234 WPB

Scopes

ASTM A234: specification for piping fitting of wrought carbon steel and alloy steel for moderate and high-temperature service.

This specification cover wrought carbon steel and steel fitting of seamless and welded construction. This specification does not cover cast welding fittings or fittings machined from casting.

Ordering information

  • Quantity,
  • Description of fitting and nominal dimensions (standard or special),
  • Steel composition by grade and class designation,
  • Construction, seamless or welded (unless seamless or welded construction is specified by the purchaser, either may be furnished at the option of the supplier),
  • Specification number (including the year/date of issue),
  • Supplementary requirements, and
  • Additional requirements

Material

  • Killed steel, forging, bars, plates, seamless or fusion-welded tubular product with filler added. “fusion-welded tubular with filler added: SAW, GTAW (filler add), GMAW”.
  • MTC shall be cleared the marking specification such number, grades and date.

If product comply other standard, the MTC shall be stated the test result values.

  • “ex. NACE MR 0175, MTC shall state hardness value, forming and heat treatment, read more in NACE MR0175 part 1, 2, 3.

Manufacture

Forging or shaping operation by cold and hot forming. NDE may be performed either prior to or after forming on welded product. NDE reports shall state in the MTC and available review by purchase.

Heat treatment

Heat treatment shall be performed after forming, see para. 7 on ASTM A960. ASTM A234 WPB most finished by normalizing, Annualizing. Other grades see section 7.0.

Chemical composition

See table 1. It is identified as trace number, heat number, casting number, or heat code.

  • L- ladle: test on casting, another name heat, casing.
  • P- product: test on production after forming, see ASTM A960 for acceptance criteria.

[Sample ASTM A234 WPB]

Limitation of carbon equivalent (CE) % = C n+ Mn/6 + (Cr+Mo+V)/5 +(Ni+Cu)/15 are in the project specification and application. Other content limitation in specification, don’t forget see any foot notes in each table.

If piping fitting formed from pipe, the MTC shall be stated “Material made from seamless pipe/welded pipe” and traceable heat number of pipe.

NDE reports such RT/UT MP/PT shall attach to MTC if fitting made from welded tubular.

Mechanical properties

See table 2 and ASTM A960. If sample test on production, the MTC shall be clearly stated the sample dimension such standard roundness, rectangle, size, subsize… or it detailed in MTC of pipe, please check with manufacturer.

If sample dimensions were not state in the MTC, elongation value shall be excess 30%.

[Sample ASTM A234 WPB]

Hardness

Fitting of all grades is allowed maximum 197 HB, except WP5, WP9, WPR, WP91, WP911.

Hydrostatic test

See ASTM A960 if PO requirement.

Dimensions

Dimension and tolerance given in ASME B16.9 for butt-weld fitting, ASTM B16.11 for threading/socket weld.

Surface quality

See ASTM A960.

Repair by welding

Most project prohibited, please check in PO requirement.

Certification

See section 17.

  • Year/date of issue shall report in the MTC, eg. ASTM A234-17 edition
  • Standard forming shall report in the MTC, eg. ASME B16.9 2012

Product markings

See MSS-P-25 and ASME B16.9, B16.11.

Supplementary

The supplementary requirements shall apply only when specified by the purchaser in the inquiry, contract, and order such as CE%, hardness, heat treatment, NDE after forming, etc.